Silica -gel transparent

High quality silica gel. Silica gel - transparent or mixed with orange is a very effective desiccant, reusable. For industry, home use and laboratories. Absorbs gases and vapors. It dries the air, removes moisture from the gases and absorbs vapors. The balls with a diameter of 3-5 mm are made of highly active silica gel with a degree of purity of min. 99.5% SiO2 (based on water-free gel). The balls are glassy in appearance, translucent, hard, odorless, insoluble and electrically non-conductive. High adsorption capacity is ensured by the area of ​​microscopic pores with an active surface area of ​​800 m2 / g. Loose desiccant reduces moisture and thus prevents the degradation of products by corrosion and mold. It is effective even at high airflow speeds. It can be regenerated and reused without significant loss of parameters. Regeneration at 130-160 ° C. When dried, the silica gel becomes transparent. Microwave drying time at 650 W is approx. 1 - 10 minutes depending on the amount and height of the silica gel layer (1 kg approx. 10 minutes)

Clear silica gel SG5, SignUS gel:
Pure silica gel - industrial and laboratory desiccant 99.5 SiO2 - silica in the form of spherical lenses with a grain size of 3-5 mm.
It offers reliable protection for electronic components and devices as well as optical components against moisture during storage and transport, drying of flowers without loss of color, smaller humid areas.
2 to 5 mm balls can be easily inserted into bags, cans, bowls, buckets, etc., and therefore can be used anywhere.
Dehumidifiers, packaging, transport packaging, drying of walls, screed, carpets and furniture, household and hobby needs, camping, sports equipment, boats / yachts, storage of filaments for 3D printing and much more.

Other areas of application and possible uses
Dehumidifiers, packaging, transport packaging, drying of walls, screed, carpets and furniture, household and hobby needs, camping, sports equipment, boats / yachts, storage of filaments for 3D printing and much more

Technical description:

Bulk density: approx. 620 - 700 g / l
Adsorption capacity (water content in% based on dead weight) at 23 (+2) ° C:
20% relative humidity = approx. 11.0%
50% relative humidity = approx. 25.5%
90% relative humidity = approx. 36.0%
Annealing losses (at 950 ° C): approx. 6.7%
Active surface: approx. 800 m2 / g
PH: 4 - 6
Pore ​​diameter: 2.0-3.0 nm
Pore ​​volume: 0.35-0.45ml / g
Thermal conductivity: 0.63KJ / m.hr

Net weight: 800 g ± 5 g
Weight including packaging: 890 g ± 5 g